Reinforced(Tanged) graphite sheet
Description
Reinforced(Tanged) graphite sheet is comprised of expanded graphite sheet and various steel sheets, such as tanged, flat or mesh. It is thermal stability, high strength and no cold flow etc. Reinforced(Tanged) graphite sheet is an ideal material of all kinds of reinforced graphite gaskets, engine heat gaskets, etc. Their are many kinds of reinforced expanded graphite sheets, such as reinforced expanded graphite sheet with SSS304/304L insert, SS316/316L insert, or tinplate insert, etc.
Suitable Working Condition
Pressure |
20MPa |
Temperature |
200-600¡æ£¨in the air£© |
Production Standard |
JB/T6628-93 |
Routine Size
Thickness£¨mm£© |
Width£¨mm£© |
Length£¨m£© |
|
Tanged Style |
Plain Metal Sheet |
<=1500 |
=<4 |
1.0~3.0 |
0.8~3.0 |
Main specification
Reinforce Material |
Configuration |
Pressure(N/mm2) |
Temperature(¡æ) |
|
Oxidizing Condition |
Non Oxidizing Condition |
|||
Tanged CS Sheet |
|
>=48 |
-10~450 |
-10~500 |
AISI304,316 Tanged (Thickness:0.1~0.127) |
|
>=48 |
-240~450 |
-200~600 |
AISI304,316 Plain Sheet) |
|
>=45 |
-240~450 |
-200~600 |
AISI304,316 Mesh |
|
>=40 |
-240~450 |
-200~600 |
¡¡
Reinforce Material |
Configuration |
Compressibility |
Recovery |
Sealing Constant(1.5mm)m1/hr |
|
N2 |
oil |
||||
Tanged CS Sheet |
|
30~35 |
15~20 |
30 |
<0.5 |
AISI304,316 Tanged (Thickness:0.1~0.127) ¡¡ |
|
30~40 |
15~30 |
60 |
<0.5 |
AISI304,316 Plain Sheet) |
|
40~50 |
10~15 |
35 |
<0.5 |
AISI304,316 Mesh |
|
30~35 |
15~20 |
7000 |
58 |
The Content of Graphic Layer
Item |
Unit |
Value |
Tolerance of Density |
g/cm3 |
-0.06~+0.06 |
Tolerance of Thickness |
mm |
-0.04~+0.04 |
C concentration |
% |
>=99 |
Tensile strength |
MPa |
4.5 |
Compressibility |
% |
>40 |
Recovery |
% |
>10 |
S concentration |
ppm |
<1100 |
Chlorine concentration |
ppm |
<45 |
Type Of Reinforced Graphite Sheet
WL-G1100 |
Tin-plate Tanged Graphite Sheet |
WL-G1110 |
SS304 Tanged Graphite Sheet |
WL-G1120 |
SS316 Tanged Graphite Sheet |
Others Can be supplied according to customer's requirement. |