Glass chopped strand mat


Description

  • Fiberglass chopped strands bound by polyester binder for hand lay process and reinforcements
  • No fuzz, dirt or impurities
  • Fast wet-out
  • Even thickness
  • Good covering and degassing properties
  • High mechanical strength and high wet strength retention
  • E-glass & C-glass chopped strand mat available


Chopped strand mat is made from fiberglass strands chopped to different lengths and bonded in one of two ways, either powder or emulsion. It is the most common form of reinforcement.

 

Application

Chopped strand mat is used primarily for hand lay-up processes, filament winding and press mould of FRP products including bathroom accessories, pipes, automobiles and other building applications.

 

Specification

1000°F / 537°C:  Fiberglass Chopped Strand Mat

Part number

Weight(g/m2)

Breakage strength(N)

Binder content (%)

WFCS100

100

≥30

15±2

WFCS120

120

≥40

12±2

WFCS150

150

≥50

6±1

WFCS180

180

≥55

5±1

WFCS200

200

≥60

4.5±0.5

WFCS225

225

≥60

4.5±0.5

WFCS250

250

≥70

4±0.5

WFCS300

300

≥70

3.8±0.5

WFCS380

380

≥80

3.5±0.5

WFCS450

450

≥90

3.3±0.5

WFCS600

600

≥100

3.3±0.5

WFCS600

900

≥150

3.3±0.5

Moisture content (%)

0.2

Bind type

Powder, emulsion

Width(mm)

Max2600, Min150,Stand 1040,1250,1270,1450

Roll weight(kg)

30, 45


Storage

  • The best conditions are temperatures between 15 and 35 degrees C and at a relative humidity between 50 and 75%, If the product is transported or stored at low temperatures (below 18 degrees C) or high temperatures (above 35 degrees C), it is advisable to condition it in the workshop at 20-25 degrees C for at least 72 hours before use to prevent condensation.Storage
  • If these conditions are respected, fiberglass products should not undergo significant changes when stored for extended periods of time